Polypropylene Concrete Reinforcing Fiber Twisted bunchy form
Product Description
Polypropylene Fiber (PP Fiber)
Denier count: 1.2D-18D
Cut length: 4mm-128mm
Features:
– It is produced by direct spinning with polymer as the raw material.
-High tenacity, few defect, good crimping performance, moderate OPU, low hot air shrinkage, good spin ability, soft and smooth hand feeling, high standards of fiber resultant yarn quality, low yarn irregularity and wide applications
– With high modulus and tenacity, low elongation, bright color and good spinnability
-Main usage: for spinning, non-woven, spunlace, sewing thread, carpet thread, etc.
1.PP Fiber Monofilament Form
Raw Material : Polypropylene
Crack Elongation : 20%±5%
Type : Monofilament
Density : 0.91±0.01 % g/cm3
Fiber Diameter : 0.02-0.05±0.005mm
Melting Point : 160—170?/p>
Tensile Strength : ≥450MPa
Resistance to Acid,Alkali : Strong
Size : 4mm,6mm,10mm,12mm,15mm,18mm,20mm,24mm,40mm
Water Absorbency : No
2.PP Fiber Mesh Form
Density(g/cm3) : 0.91
Elastic Modulas (MPa) : >3500
Length(mm) : 6mm,10mm,12mm,15mm,20mm,50mm
Equivalent Diameter (m) : 100
Shape : Beam-like Net
Crack Elongation(%) : ≥10
Acid &Alkali Resistance : Strong
Water-Absorbency : No
Tensile Strength(MPa) : 346-560
Melting Point(C) : 160—170
3.PP Fiber Bunchy Twisted Form
Density(g/cm3) : 0.91
Elastic Modulus ( MPa) : >5000
Length(mm) : 54mm
Equivalent Dia (mm) : 0.3+/- 0.05
Shape : bundle-like and twisted
Break tensile Ratio(%) : >15
Break Strength(MPa) : >560
Resistance to acid, alkali : strong
4.Curved PP Macro Fiber
Density(g/cm3) : 0.91
Elastic Modulas (MPa) : >5000
Length(mm) : 30mm,40mm,50mm
Equivalent Dia(μm) : 80,100
Shape : curved bar
Break Tensile Ratio(%) : ≤155
Break Strength(MPa) : ≥460
Melt Point : ≥160