Supply High quality thermoplastic road marking paint
High quality thermoplastic road marking paint
| Test Items | Technical requirements | Test results | ||
| Density | 1.8-2.3 | 2.01 qualified | ||
| Softing point(oC) | 90-125 | 105 qualified | ||
| The film color and appearance | after drying,no Wrinkles, spots, foam, crack, fall off, sticky tire phenomenon,The color and appearance of film almost same with the sdandard color sample. | qualified | ||
| Dry time no wheel | <=3 | 3 qualified | ||
| Chromaticity performance
|
white | chromaticity coordinates(x,y) | Inside following four corners chromaticity coordinates’s the quadrilateral(0.350,0.360);(0.300,0.310);(0.290,0.320);(0.340,0.370) | X:0.318
Y:0.336 |
| luminance factor | >=0.75 | 0.83 | ||
| yellow | chromaticity coordinates | Inside following four corners chromaticity coordinates’s the quadrilateral(0.519,0.480);(0.468,0.442);(0.427,0.483);(0.465,0.534) | X:0.485
Y:0.470 |
|
| luminance factor | >=0.45 | 0.50 | ||
| Compressive strength(MPa) | >=12 | 18.2 | ||
| Wearing resistance(mg)
(200rotate/1000g after weight reduction) |
<=80(JM-100rubber grindingwheel) | 51.7 | ||
Thermoplastic Road Marking Paint without glass bead
| Test Items | Technical requirements | Test results | ||
| Density | 1.8-2.3 | 2.01 qualified | ||
| Softing point(oC) | 90-125 | 105 qualified | ||
| The film color and appearance | after drying,no Wrinkles, spots, foam, crack, fall off, sticky tire phenomenon,The color and appearance of film almost same with the sdandard color sample. | qualified | ||
| Dry time no wheel | <=3 | 3 qualified | ||
| Chromaticity performance
|
white | chromaticity coordinates(x,y) | Inside following four corners chromaticity coordinates’s the quadrilateral(0.350,0.360);(0.300,0.310);(0.290,0.320);(0.340,0.370) | X:0.318
Y:0.336 |
| luminance factor | >=0.75 | 0.83 | ||
| yellow | chromaticity coordinates | Inside following four corners chromaticity coordinates’s the quadrilateral(0.519,0.480);(0.468,0.442);(0.427,0.483);(0.465,0.534) | X:0.485
Y:0.470 |
|
| luminance factor | >=0.45 | 0.50 | ||
| Compressive strength(MPa) | >=12 | 18.2 | ||
| Wearing resistance(mg)
(200rotate/1000g after weight reduction) |
<=80(JM-100rubber grinding wheel) | 51.7 | ||